SAE-AISI 4621 Steel vs. EN 1.0601 Steel

Both SAE-AISI 4621 steel and EN 1.0601 steel are iron alloys. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI 4621 steel and the bottom bar is EN 1.0601 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
11
Fatigue Strength, MPa 270
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Shear Strength, MPa 320
430
Tensile Strength: Ultimate (UTS), MPa 500
730
Tensile Strength: Yield (Proof), MPa 360
350

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
48
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 3.3
2.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.5
Embodied Energy, MJ/kg 22
19
Embodied Water, L/kg 50
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
65
Resilience: Unit (Modulus of Resilience), kJ/m3 340
330
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
26
Strength to Weight: Bending, points 18
23
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 15
23

Alloy Composition

Carbon (C), % 0.18 to 0.23
0.57 to 0.65
Chromium (Cr), % 0
0 to 0.4
Iron (Fe), % 96.1 to 97.1
97.1 to 98.8
Manganese (Mn), % 0.7 to 0.9
0.6 to 0.9
Molybdenum (Mo), % 0.2 to 0.3
0 to 0.1
Nickel (Ni), % 1.7 to 2.0
0 to 0.4
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0.15 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.045