SAE-AISI 4621 Steel vs. EN 1.4319 Stainless Steel

Both SAE-AISI 4621 steel and EN 1.4319 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4621 steel and the bottom bar is EN 1.4319 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 27
51
Fatigue Strength, MPa 270
240
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 320
460
Tensile Strength: Ultimate (UTS), MPa 500
640
Tensile Strength: Yield (Proof), MPa 360
250

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 410
890
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 46
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 3.3
13
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.6
2.7
Embodied Energy, MJ/kg 22
39
Embodied Water, L/kg 50
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
260
Resilience: Unit (Modulus of Resilience), kJ/m3 340
160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
23
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 12
4.0
Thermal Shock Resistance, points 15
14

Alloy Composition

Carbon (C), % 0.18 to 0.23
0 to 0.070
Chromium (Cr), % 0
16 to 18
Iron (Fe), % 96.1 to 97.1
70.8 to 78
Manganese (Mn), % 0.7 to 0.9
0 to 2.0
Molybdenum (Mo), % 0.2 to 0.3
0
Nickel (Ni), % 1.7 to 2.0
6.0 to 8.0
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.030