SAE-AISI 4621 Steel vs. EN 1.4597 Stainless Steel

Both SAE-AISI 4621 steel and EN 1.4597 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4621 steel and the bottom bar is EN 1.4597 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
45
Fatigue Strength, MPa 270
300
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 320
470
Tensile Strength: Ultimate (UTS), MPa 500
680
Tensile Strength: Yield (Proof), MPa 360
330

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 410
860
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 46
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 3.3
11
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.6
2.5
Embodied Energy, MJ/kg 22
36
Embodied Water, L/kg 50
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
250
Resilience: Unit (Modulus of Resilience), kJ/m3 340
280
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
25
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 12
4.1
Thermal Shock Resistance, points 15
15

Alloy Composition

Carbon (C), % 0.18 to 0.23
0 to 0.1
Chromium (Cr), % 0
15 to 18
Copper (Cu), % 0
2.0 to 3.5
Iron (Fe), % 96.1 to 97.1
63 to 76.4
Manganese (Mn), % 0.7 to 0.9
6.5 to 9.0
Molybdenum (Mo), % 0.2 to 0.3
0 to 1.0
Nickel (Ni), % 1.7 to 2.0
0 to 3.0
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 2.0
Sulfur (S), % 0 to 0.040
0 to 0.030