SAE-AISI 94B17 Steel vs. ACI-ASTM CD3MN Steel

Both SAE-AISI 94B17 steel and ACI-ASTM CD3MN steel are iron alloys. They have 69% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 94B17 steel and the bottom bar is ACI-ASTM CD3MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
29
Fatigue Strength, MPa 200
340
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 440
710
Tensile Strength: Yield (Proof), MPa 270
460

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 410
1060
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
16
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
18
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
3.6
Embodied Energy, MJ/kg 20
50
Embodied Water, L/kg 49
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
180
Resilience: Unit (Modulus of Resilience), kJ/m3 200
530
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
25
Strength to Weight: Bending, points 16
23
Thermal Diffusivity, mm2/s 10
4.3
Thermal Shock Resistance, points 13
20

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.15 to 0.2
0 to 0.030
Chromium (Cr), % 0.3 to 0.5
21 to 23.5
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 97.1 to 98.3
62.6 to 71.9
Manganese (Mn), % 0.75 to 1.0
0 to 1.5
Molybdenum (Mo), % 0.080 to 0.15
2.5 to 3.5
Nickel (Ni), % 0.3 to 0.6
4.5 to 6.5
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.020