SAE-AISI 94B17 Steel vs. ASTM A182 Grade F5

Both SAE-AISI 94B17 steel and ASTM A182 grade F5 are iron alloys. Both are furnished in the annealed condition. They have a moderately high 95% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 94B17 steel and the bottom bar is ASTM A182 grade F5.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25
22
Fatigue Strength, MPa 200
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Shear Strength, MPa 280
340
Tensile Strength: Ultimate (UTS), MPa 440
540
Tensile Strength: Yield (Proof), MPa 270
310

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 410
510
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
4.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.8
Embodied Energy, MJ/kg 20
24
Embodied Water, L/kg 49
69

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
100
Resilience: Unit (Modulus of Resilience), kJ/m3 200
260
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
19
Strength to Weight: Bending, points 16
19
Thermal Diffusivity, mm2/s 10
11
Thermal Shock Resistance, points 13
15

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.15 to 0.2
0 to 0.15
Chromium (Cr), % 0.3 to 0.5
4.0 to 6.0
Iron (Fe), % 97.1 to 98.3
91.5 to 95.3
Manganese (Mn), % 0.75 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 0.080 to 0.15
0.44 to 0.65
Nickel (Ni), % 0.3 to 0.6
0 to 0.5
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0.15 to 0.35
0 to 0.5
Sulfur (S), % 0 to 0.040
0 to 0.030