SAE-AISI 94B17 Steel vs. EN 1.0033 Steel

Both SAE-AISI 94B17 steel and EN 1.0033 steel are iron alloys. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI 94B17 steel and the bottom bar is EN 1.0033 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
86 to 96
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25
17 to 32
Fatigue Strength, MPa 200
120 to 140
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 280
200
Tensile Strength: Ultimate (UTS), MPa 440
300 to 330
Tensile Strength: Yield (Proof), MPa 270
150 to 200

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
400
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.4
Embodied Energy, MJ/kg 20
18
Embodied Water, L/kg 49
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
48 to 83
Resilience: Unit (Modulus of Resilience), kJ/m3 200
63 to 100
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
10 to 12
Strength to Weight: Bending, points 16
13 to 14
Thermal Diffusivity, mm2/s 10
14
Thermal Shock Resistance, points 13
9.4 to 10

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.15 to 0.2
0 to 0.11
Chromium (Cr), % 0.3 to 0.5
0
Iron (Fe), % 97.1 to 98.3
98.8 to 100
Manganese (Mn), % 0.75 to 1.0
0 to 0.7
Molybdenum (Mo), % 0.080 to 0.15
0
Nickel (Ni), % 0.3 to 0.6
0
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0.15 to 0.35
0 to 0.35
Sulfur (S), % 0 to 0.040
0 to 0.045