SAE-AISI 94B17 Steel vs. EN 1.4419 Stainless Steel

Both SAE-AISI 94B17 steel and EN 1.4419 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 94B17 steel and the bottom bar is EN 1.4419 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
11 to 17
Fatigue Strength, MPa 200
230 to 680
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 280
410 to 950
Tensile Strength: Ultimate (UTS), MPa 440
660 to 1590
Tensile Strength: Yield (Proof), MPa 270
370 to 1240

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 410
790
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
30
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
8.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.5
2.2
Embodied Energy, MJ/kg 20
30
Embodied Water, L/kg 49
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
95 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 200
350 to 3920
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
24 to 57
Strength to Weight: Bending, points 16
22 to 39
Thermal Diffusivity, mm2/s 10
8.1
Thermal Shock Resistance, points 13
23 to 55

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.15 to 0.2
0.36 to 0.42
Chromium (Cr), % 0.3 to 0.5
13 to 14.5
Iron (Fe), % 97.1 to 98.3
82 to 86
Manganese (Mn), % 0.75 to 1.0
0 to 1.0
Molybdenum (Mo), % 0.080 to 0.15
0.6 to 1.0
Nickel (Ni), % 0.3 to 0.6
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015