SAE-AISI 94B17 Steel vs. EN 1.4460 Stainless Steel

Both SAE-AISI 94B17 steel and EN 1.4460 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 94B17 steel and the bottom bar is EN 1.4460 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
220
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
21
Fatigue Strength, MPa 200
330
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Shear Strength, MPa 280
470
Tensile Strength: Ultimate (UTS), MPa 440
750
Tensile Strength: Yield (Proof), MPa 270
510

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 410
1100
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
18
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.5
3.4
Embodied Energy, MJ/kg 20
48
Embodied Water, L/kg 49
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
140
Resilience: Unit (Modulus of Resilience), kJ/m3 200
640
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
27
Strength to Weight: Bending, points 16
24
Thermal Diffusivity, mm2/s 10
4.0
Thermal Shock Resistance, points 13
20

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.15 to 0.2
0 to 0.050
Chromium (Cr), % 0.3 to 0.5
25 to 28
Iron (Fe), % 97.1 to 98.3
60.2 to 69.2
Manganese (Mn), % 0.75 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.080 to 0.15
1.3 to 2.0
Nickel (Ni), % 0.3 to 0.6
4.5 to 6.5
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015