SAE-AISI 94B17 Steel vs. EN 1.4852 Stainless Steel

Both SAE-AISI 94B17 steel and EN 1.4852 stainless steel are iron alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 94B17 steel and the bottom bar is EN 1.4852 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
140
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
4.6
Fatigue Strength, MPa 200
120
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 440
490
Tensile Strength: Yield (Proof), MPa 270
250

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Maximum Temperature: Mechanical, °C 410
1100
Melting Completion (Liquidus), °C 1460
1380
Melting Onset (Solidus), °C 1420
1340
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
13
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
41
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
6.9
Embodied Energy, MJ/kg 20
100
Embodied Water, L/kg 49
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
19
Resilience: Unit (Modulus of Resilience), kJ/m3 200
160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
17
Strength to Weight: Bending, points 16
18
Thermal Diffusivity, mm2/s 10
3.4
Thermal Shock Resistance, points 13
11

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.15 to 0.2
0.3 to 0.5
Chromium (Cr), % 0.3 to 0.5
24 to 27
Iron (Fe), % 97.1 to 98.3
29.6 to 40.9
Manganese (Mn), % 0.75 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.080 to 0.15
0 to 0.5
Nickel (Ni), % 0.3 to 0.6
33 to 36
Niobium (Nb), % 0
0.8 to 1.8
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
1.0 to 2.5
Sulfur (S), % 0 to 0.040
0 to 0.030