SAE-AISI 94B17 Steel vs. SAE-AISI 1137 Steel

Both SAE-AISI 94B17 steel and SAE-AISI 1137 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 94B17 steel and the bottom bar is SAE-AISI 1137 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
200 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25
11 to 17
Fatigue Strength, MPa 200
250 to 400
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 280
430 to 460
Tensile Strength: Ultimate (UTS), MPa 440
700 to 760
Tensile Strength: Yield (Proof), MPa 270
370 to 650

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
10
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.4
Embodied Energy, MJ/kg 20
19
Embodied Water, L/kg 49
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
81 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 200
360 to 1130
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
25 to 27
Strength to Weight: Bending, points 16
22 to 24
Thermal Diffusivity, mm2/s 10
14
Thermal Shock Resistance, points 13
21 to 23

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.15 to 0.2
0.32 to 0.39
Chromium (Cr), % 0.3 to 0.5
0
Iron (Fe), % 97.1 to 98.3
97.8 to 98.3
Manganese (Mn), % 0.75 to 1.0
1.4 to 1.7
Molybdenum (Mo), % 0.080 to 0.15
0
Nickel (Ni), % 0.3 to 0.6
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0
Sulfur (S), % 0 to 0.040
0.080 to 0.13