SAE-AISI 94B30 Steel vs. S44537 Stainless Steel

Both SAE-AISI 94B30 steel and S44537 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 75% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 94B30 steel and the bottom bar is S44537 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
21
Fatigue Strength, MPa 220
230
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
79
Shear Strength, MPa 320
320
Tensile Strength: Ultimate (UTS), MPa 500
510
Tensile Strength: Yield (Proof), MPa 300
360

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 410
1000
Melting Completion (Liquidus), °C 1460
1480
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
21
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
3.4
Embodied Energy, MJ/kg 20
50
Embodied Water, L/kg 49
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
95
Resilience: Unit (Modulus of Resilience), kJ/m3 250
320
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
18
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 10
5.6
Thermal Shock Resistance, points 15
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.28 to 0.33
0 to 0.030
Chromium (Cr), % 0.3 to 0.5
20 to 24
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 97 to 98.1
69 to 78.6
Lanthanum (La), % 0
0.040 to 0.2
Manganese (Mn), % 0.75 to 1.0
0 to 0.8
Molybdenum (Mo), % 0.080 to 0.15
0
Nickel (Ni), % 0.3 to 0.6
0 to 0.5
Niobium (Nb), % 0
0.2 to 1.0
Nitrogen (N), % 0
0 to 0.040
Phosphorus (P), % 0 to 0.035
0 to 0.050
Silicon (Si), % 0.15 to 0.35
0.1 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.0060
Titanium (Ti), % 0
0.020 to 0.2
Tungsten (W), % 0
1.0 to 3.0