SAE-AISI D2 Steel vs. C82200 Copper
SAE-AISI D2 steel belongs to the iron alloys classification, while C82200 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI D2 steel and the bottom bar is C82200 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 5.0 to 16 | |
| 8.0 to 20 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 75 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 760 to 2000 | |
| 390 to 660 |
| Tensile Strength: Yield (Proof), MPa | 470 to 1510 | |
| 210 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 220 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1080 |
| Melting Onset (Solidus), °C | 1390 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 31 | |
| 180 |
| Thermal Expansion, µm/m-K | 11 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.3 | |
| 45 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.1 | |
| 46 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 55 |
| Density, g/cm3 | 7.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 4.8 |
| Embodied Energy, MJ/kg | 50 | |
| 74 |
| Embodied Water, L/kg | 100 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 92 to 100 | |
| 49 to 66 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 570 to 5940 | |
| 180 to 1130 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 27 to 72 | |
| 12 to 20 |
| Strength to Weight: Bending, points | 24 to 46 | |
| 13 to 19 |
| Thermal Diffusivity, mm2/s | 8.3 | |
| 53 |
| Thermal Shock Resistance, points | 25 to 67 | |
| 14 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Beryllium (Be), % | 0 | |
| 0.35 to 0.8 |
| Carbon (C), % | 1.4 to 1.6 | |
| 0 |
| Chromium (Cr), % | 11 to 13 | |
| 0 |
| Cobalt (Co), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 to 0.25 | |
| 97.4 to 98.7 |
| Iron (Fe), % | 81.3 to 86.9 | |
| 0 |
| Manganese (Mn), % | 0 to 0.6 | |
| 0 |
| Molybdenum (Mo), % | 0.7 to 1.2 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 1.0 to 2.0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Vanadium (V), % | 0 to 1.1 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |