SAE-AISI H42 Steel vs. AWS E630
Both SAE-AISI H42 steel and AWS E630 are iron alloys. They have 79% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI H42 steel and the bottom bar is AWS E630.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 1980 | |
| 1040 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 280 |
| Melting Completion (Liquidus), °C | 1620 | |
| 1430 |
| Melting Onset (Solidus), °C | 1570 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Conductivity, W/m-K | 24 | |
| 17 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 14 |
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.8 | |
| 2.8 |
| Embodied Energy, MJ/kg | 130 | |
| 40 |
| Embodied Water, L/kg | 98 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 31 | |
| 18 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 23 to 65 | |
| 37 |
| Strength to Weight: Bending, points | 21 to 42 | |
| 29 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 4.5 |
| Thermal Shock Resistance, points | 20 to 57 | |
| 28 |
Alloy Composition
| Carbon (C), % | 0.55 to 0.7 | |
| 0 to 0.050 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 16 to 16.8 |
| Copper (Cu), % | 0 to 0.25 | |
| 3.3 to 4.0 |
| Iron (Fe), % | 79.3 to 83.8 | |
| 71.6 to 75.9 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0.25 to 0.75 |
| Molybdenum (Mo), % | 4.5 to 5.5 | |
| 0 to 0.75 |
| Nickel (Ni), % | 0 to 0.3 | |
| 4.5 to 5.0 |
| Niobium (Nb), % | 0 | |
| 0.15 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 5.5 to 6.8 | |
| 0 |
| Vanadium (V), % | 1.8 to 2.2 | |
| 0 |