SAE-AISI H43 Steel vs. EN 1.8918 Steel

Both SAE-AISI H43 steel and EN 1.8918 steel are iron alloys. They have 86% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H43 steel and the bottom bar is EN 1.8918 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 710 to 2140
640

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Melting Completion (Liquidus), °C 1530
1460
Melting Onset (Solidus), °C 1480
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 30
46
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 14
2.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 8.2
1.7
Embodied Energy, MJ/kg 120
24
Embodied Water, L/kg 100
51

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 75
23
Strength to Weight: Bending, points 22 to 46
21
Thermal Diffusivity, mm2/s 8.3
12
Thermal Shock Resistance, points 21 to 62
19

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.050
Carbon (C), % 0.5 to 0.65
0 to 0.2
Chromium (Cr), % 3.8 to 4.5
0 to 0.3
Copper (Cu), % 0
0 to 0.7
Iron (Fe), % 83.2 to 85.9
95.2 to 98.9
Manganese (Mn), % 0.15 to 0.4
1.1 to 1.7
Molybdenum (Mo), % 7.8 to 8.5
0 to 0.1
Nickel (Ni), % 0
0 to 0.8
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.025
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0.2 to 0.45
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.0050
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 1.8 to 2.2
0 to 0.2