Both SAE-AISI M36 steel and K94200 alloy are iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M36 steel and the bottom bar is K94200 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
140
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 78
54
Tensile Strength: Ultimate (UTS), MPa 810 to 2190
500 to 710

Thermal Properties

Melting Onset (Solidus), °C 1550
1440
Specific Heat Capacity, J/kg-K 440
500
Thermal Conductivity, W/m-K 19
15
Thermal Expansion, µm/m-K 12
5.0

Otherwise Unclassified Properties

Density, g/cm3 8.4
8.2

Common Calculations

Stiffness to Weight: Axial, points 13
9.8
Stiffness to Weight: Bending, points 23
21
Strength to Weight: Axial, points 27 to 72
17 to 24
Strength to Weight: Bending, points 23 to 44
17 to 22
Thermal Diffusivity, mm2/s 5.1
3.7
Thermal Shock Resistance, points 25 to 68
49 to 70