SAE-AISI M41 Steel vs. AISI W1 Steel
Both SAE-AISI M41 steel and AISI W1 steel are iron alloys. They have 78% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M41 steel and the bottom bar is AISI W1 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 800 to 2290 | |
| 590 to 2320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Melting Completion (Liquidus), °C | 1600 | |
| 1450 |
| Melting Onset (Solidus), °C | 1550 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Conductivity, W/m-K | 22 | |
| 48 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 2.2 |
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 9.1 | |
| 1.6 |
| Embodied Energy, MJ/kg | 140 | |
| 21 |
| Embodied Water, L/kg | 120 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 26 to 76 | |
| 21 to 83 |
| Strength to Weight: Bending, points | 23 to 46 | |
| 20 to 50 |
| Thermal Diffusivity, mm2/s | 6.0 | |
| 13 |
| Thermal Shock Resistance, points | 25 to 71 | |
| 22 to 85 |
Alloy Composition
| Carbon (C), % | 1.1 to 1.2 | |
| 0.7 to 1.5 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 0 to 0.15 |
| Cobalt (Co), % | 4.8 to 5.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.2 |
| Iron (Fe), % | 73.4 to 78.9 | |
| 96.4 to 98.9 |
| Manganese (Mn), % | 0.2 to 0.6 | |
| 0.35 to 0.73 |
| Molybdenum (Mo), % | 3.3 to 4.3 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.15 to 0.5 | |
| 0.1 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |
| Tungsten (W), % | 6.3 to 7.0 | |
| 0 to 0.15 |
| Vanadium (V), % | 1.8 to 2.3 | |
| 0 to 0.1 |