SAE-AISI M41 Steel vs. Nickel 601
SAE-AISI M41 steel belongs to the iron alloys classification, while nickel 601 belongs to the nickel alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M41 steel and the bottom bar is nickel 601.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 800 to 2290 | |
| 660 to 890 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 320 |
| Melting Completion (Liquidus), °C | 1600 | |
| 1410 |
| Melting Onset (Solidus), °C | 1550 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Conductivity, W/m-K | 22 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 49 |
| Density, g/cm3 | 8.4 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 9.1 | |
| 8.0 |
| Embodied Energy, MJ/kg | 140 | |
| 110 |
| Embodied Water, L/kg | 120 | |
| 280 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 26 to 76 | |
| 22 to 30 |
| Strength to Weight: Bending, points | 23 to 46 | |
| 20 to 25 |
| Thermal Diffusivity, mm2/s | 6.0 | |
| 2.8 |
| Thermal Shock Resistance, points | 25 to 71 | |
| 17 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 1.0 to 1.7 |
| Carbon (C), % | 1.1 to 1.2 | |
| 0 to 0.1 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 21 to 25 |
| Cobalt (Co), % | 4.8 to 5.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 1.0 |
| Iron (Fe), % | 73.4 to 78.9 | |
| 7.7 to 20 |
| Manganese (Mn), % | 0.2 to 0.6 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 3.3 to 4.3 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 58 to 63 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Tungsten (W), % | 6.3 to 7.0 | |
| 0 |
| Vanadium (V), % | 1.8 to 2.3 | |
| 0 |