SAE-AISI M42 Steel vs. AWS E80C-Ni3

Both SAE-AISI M42 steel and AWS E80C-Ni3 are iron alloys. They have 80% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M42 steel and the bottom bar is AWS E80C-Ni3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 78
72
Tensile Strength: Ultimate (UTS), MPa 810 to 2310
630

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Melting Completion (Liquidus), °C 1540
1450
Melting Onset (Solidus), °C 1490
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 20
51
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 30
3.9
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 7.4
1.7
Embodied Energy, MJ/kg 100
23
Embodied Water, L/kg 140
53

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 28 to 79
22
Strength to Weight: Bending, points 24 to 48
21
Thermal Diffusivity, mm2/s 5.4
14
Thermal Shock Resistance, points 25 to 71
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 1.1 to 1.2
0 to 0.12
Chromium (Cr), % 3.5 to 4.3
0
Cobalt (Co), % 7.8 to 8.8
0
Copper (Cu), % 0 to 0.25
0 to 0.35
Iron (Fe), % 76.3 to 81
92.8 to 97.3
Manganese (Mn), % 0.15 to 0.4
0 to 1.5
Molybdenum (Mo), % 9.0 to 10
0
Nickel (Ni), % 0 to 0.3
2.8 to 3.8
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.15 to 0.65
0 to 0.9
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 1.2 to 1.9
0
Vanadium (V), % 1.0 to 1.4
0 to 0.030
Residuals, % 0
0 to 0.5