SAE-AISI M44 Steel vs. C10400 Copper
SAE-AISI M44 steel belongs to the iron alloys classification, while C10400 copper belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M44 steel and the bottom bar is C10400 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 78 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 2290 | |
| 230 to 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 210 |
| Melting Completion (Liquidus), °C | 1590 | |
| 1080 |
| Melting Onset (Solidus), °C | 1540 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 390 |
| Thermal Conductivity, W/m-K | 14 | |
| 390 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 43 | |
| 32 |
| Density, g/cm3 | 8.4 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 9.9 | |
| 2.6 |
| Embodied Energy, MJ/kg | 150 | |
| 42 |
| Embodied Water, L/kg | 170 | |
| 340 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 23 | |
| 18 |
| Strength to Weight: Axial, points | 28 to 75 | |
| 7.2 to 13 |
| Strength to Weight: Bending, points | 24 to 46 | |
| 9.4 to 14 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 110 |
| Thermal Shock Resistance, points | 27 to 70 | |
| 8.2 to 15 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 1.1 to 1.2 | |
| 0 |
| Chromium (Cr), % | 4.0 to 4.8 | |
| 0 |
| Cobalt (Co), % | 11 to 12.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 99.9 to 99.973 |
| Iron (Fe), % | 65.3 to 70.6 | |
| 0 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0 |
| Molybdenum (Mo), % | 6.0 to 7.0 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Oxygen (O), % | 0 | |
| 0 to 0.0010 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0.3 to 0.55 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0.027 to 0.050 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 5.0 to 5.8 | |
| 0 |
| Vanadium (V), % | 1.9 to 2.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.050 |