SAE-AISI M47 Steel vs. SAE-AISI M41 Steel
Both SAE-AISI M47 steel and SAE-AISI M41 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common.
For each property being compared, the top bar is SAE-AISI M47 steel and the bottom bar is SAE-AISI M41 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 810 to 2310 | |
| 800 to 2290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 260 |
| Melting Completion (Liquidus), °C | 1540 | |
| 1600 |
| Melting Onset (Solidus), °C | 1500 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 440 |
| Thermal Conductivity, W/m-K | 23 | |
| 22 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 33 |
| Density, g/cm3 | 8.1 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 9.1 |
| Embodied Energy, MJ/kg | 100 | |
| 140 |
| Embodied Water, L/kg | 120 | |
| 120 |
Common Calculations
| PREN (Pitting Resistance) | 38 | |
| 28 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 28 to 79 | |
| 26 to 76 |
| Strength to Weight: Bending, points | 24 to 48 | |
| 23 to 46 |
| Thermal Diffusivity, mm2/s | 6.3 | |
| 6.0 |
| Thermal Shock Resistance, points | 27 to 77 | |
| 25 to 71 |
Alloy Composition
| Carbon (C), % | 1.1 to 1.2 | |
| 1.1 to 1.2 |
| Chromium (Cr), % | 3.5 to 4.0 | |
| 3.8 to 4.5 |
| Cobalt (Co), % | 4.8 to 5.3 | |
| 4.8 to 5.8 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 78.7 to 85 | |
| 73.4 to 78.9 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0.2 to 0.6 |
| Molybdenum (Mo), % | 9.3 to 10 | |
| 3.3 to 4.3 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.2 to 0.45 | |
| 0.15 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 1.3 to 1.8 | |
| 6.3 to 7.0 |
| Vanadium (V), % | 1.2 to 1.4 | |
| 1.8 to 2.3 |