SAE-AISI M52 Steel vs. SAE-AISI M36 Steel

Both SAE-AISI M52 steel and SAE-AISI M36 steel are iron alloys. They have 86% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M52 steel and the bottom bar is SAE-AISI M36 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
78
Tensile Strength: Ultimate (UTS), MPa 710 to 2280
810 to 2190

Thermal Properties

Latent Heat of Fusion, J/g 260
260
Melting Completion (Liquidus), °C 1510
1600
Melting Onset (Solidus), °C 1470
1550
Specific Heat Capacity, J/kg-K 460
440
Thermal Conductivity, W/m-K 31
19
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 12
38
Density, g/cm3 7.9
8.4
Embodied Carbon, kg CO2/kg material 7.5
9.5
Embodied Energy, MJ/kg 110
140
Embodied Water, L/kg 89
140

Common Calculations

PREN (Pitting Resistance) 20
31
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 25 to 80
27 to 72
Strength to Weight: Bending, points 22 to 49
23 to 44
Thermal Diffusivity, mm2/s 8.4
5.1
Thermal Shock Resistance, points 21 to 67
25 to 68

Alloy Composition

Carbon (C), % 0.85 to 1.0
0.8 to 0.9
Chromium (Cr), % 3.5 to 4.3
3.8 to 4.5
Cobalt (Co), % 0
7.8 to 8.8
Copper (Cu), % 0 to 0.25
0 to 0.25
Iron (Fe), % 84.4 to 88.9
70.1 to 75.5
Manganese (Mn), % 0.15 to 0.45
0.15 to 0.4
Molybdenum (Mo), % 4.0 to 4.9
4.6 to 5.5
Nickel (Ni), % 0 to 0.3
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.2 to 0.6
0.2 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.75 to 1.5
5.5 to 6.5
Vanadium (V), % 1.7 to 2.3
1.8 to 2.3

Comparable Variants