SAE-AISI M52 Steel vs. SAE-AISI S5 Steel

Both SAE-AISI M52 steel and SAE-AISI S5 steel are iron alloys. They have 89% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI M52 steel and the bottom bar is SAE-AISI S5 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
72
Tensile Strength: Ultimate (UTS), MPa 710 to 2280
680 to 1940

Thermal Properties

Latent Heat of Fusion, J/g 260
280
Melting Completion (Liquidus), °C 1510
1440
Melting Onset (Solidus), °C 1470
1400
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 31
42
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.9
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 10
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
3.1
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 7.5
2.1
Embodied Energy, MJ/kg 110
29
Embodied Water, L/kg 89
51

Common Calculations

PREN (Pitting Resistance) 20
2.9
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 80
25 to 70
Strength to Weight: Bending, points 22 to 49
22 to 45
Thermal Diffusivity, mm2/s 8.4
11
Thermal Shock Resistance, points 21 to 67
23 to 65

Alloy Composition

Carbon (C), % 0.85 to 1.0
0.5 to 0.65
Chromium (Cr), % 3.5 to 4.3
0 to 0.5
Copper (Cu), % 0 to 0.25
0 to 0.25
Iron (Fe), % 84.4 to 88.9
93.6 to 97
Manganese (Mn), % 0.15 to 0.45
0.6 to 1.0
Molybdenum (Mo), % 4.0 to 4.9
0.2 to 1.4
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.2 to 0.6
1.8 to 2.3
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.75 to 1.5
0
Vanadium (V), % 1.7 to 2.3
0 to 0.35

Comparable Variants