SAE-AISI T2 Steel vs. SAE-AISI H23 Steel
Both SAE-AISI T2 steel and SAE-AISI H23 steel are iron alloys. They have a moderately high 92% of their average alloy composition in common.
For each property being compared, the top bar is SAE-AISI T2 steel and the bottom bar is SAE-AISI H23 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 79 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 2150 | |
| 760 to 1550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Melting Completion (Liquidus), °C | 1820 | |
| 1680 |
| Melting Onset (Solidus), °C | 1760 | |
| 1630 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 440 |
| Thermal Conductivity, W/m-K | 19 | |
| 20 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 46 | |
| 34 |
| Density, g/cm3 | 9.3 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 6.9 |
| Embodied Energy, MJ/kg | 170 | |
| 110 |
| Embodied Water, L/kg | 98 | |
| 120 |
Common Calculations
| PREN (Pitting Resistance) | 36 | |
| 32 |
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 22 |
| Strength to Weight: Axial, points | 23 to 64 | |
| 24 to 49 |
| Strength to Weight: Bending, points | 20 to 40 | |
| 21 to 34 |
| Thermal Diffusivity, mm2/s | 4.9 | |
| 5.2 |
| Thermal Shock Resistance, points | 23 to 65 | |
| 23 to 47 |
Alloy Composition
| Carbon (C), % | 0.8 to 0.9 | |
| 0.25 to 0.35 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 11 to 12.8 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 70.8 to 75.8 | |
| 71.3 to 76.7 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.2 to 0.4 | |
| 0.15 to 0.6 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 17.5 to 19 | |
| 11 to 12.8 |
| Vanadium (V), % | 1.8 to 2.4 | |
| 0.75 to 1.3 |