Titanium 4-4-2 vs. SAE-AISI D2 Steel
Titanium 4-4-2 belongs to the titanium alloys classification, while SAE-AISI D2 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is titanium 4-4-2 and the bottom bar is SAE-AISI D2 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 10 | |
| 5.0 to 16 |
| Fatigue Strength, MPa | 590 to 620 | |
| 310 to 860 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 75 |
| Shear Strength, MPa | 690 to 750 | |
| 460 to 1160 |
| Tensile Strength: Ultimate (UTS), MPa | 1150 to 1250 | |
| 760 to 2000 |
| Tensile Strength: Yield (Proof), MPa | 1030 to 1080 | |
| 470 to 1510 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 270 |
| Melting Completion (Liquidus), °C | 1610 | |
| 1440 |
| Melting Onset (Solidus), °C | 1560 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 480 |
| Thermal Conductivity, W/m-K | 6.7 | |
| 31 |
| Thermal Expansion, µm/m-K | 8.6 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 39 | |
| 8.0 |
| Density, g/cm3 | 4.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 30 | |
| 3.4 |
| Embodied Energy, MJ/kg | 480 | |
| 50 |
| Embodied Water, L/kg | 180 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
| 92 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 4700 to 5160 | |
| 570 to 5940 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 34 | |
| 25 |
| Strength to Weight: Axial, points | 68 to 74 | |
| 27 to 72 |
| Strength to Weight: Bending, points | 52 to 55 | |
| 24 to 46 |
| Thermal Diffusivity, mm2/s | 2.6 | |
| 8.3 |
| Thermal Shock Resistance, points | 86 to 93 | |
| 25 to 67 |
Alloy Composition
| Aluminum (Al), % | 3.0 to 5.0 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 1.4 to 1.6 |
| Chromium (Cr), % | 0 | |
| 11 to 13 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 81.3 to 86.9 |
| Manganese (Mn), % | 0 | |
| 0 to 0.6 |
| Molybdenum (Mo), % | 3.0 to 5.0 | |
| 0.7 to 1.2 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Oxygen (O), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.3 to 0.7 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 1.5 to 2.5 | |
| 0 |
| Titanium (Ti), % | 85.8 to 92.2 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0 to 1.1 |
| Residuals, % | 0 to 0.4 | |
| 0 |