Type 1 Magnetic Alloy vs. ASTM Grade HL Steel
Both Type 1 magnetic alloy and ASTM grade HL steel are iron alloys. They have 68% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is Type 1 magnetic alloy and the bottom bar is ASTM grade HL steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 4.0 to 38 | |
| 11 |
| Poisson's Ratio | 0.3 | |
| 0.27 |
| Shear Modulus, GPa | 72 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 830 | |
| 500 |
| Tensile Strength: Yield (Proof), MPa | 220 to 790 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 320 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1390 |
| Melting Onset (Solidus), °C | 1370 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 490 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 27 |
| Density, g/cm3 | 8.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 5.6 | |
| 4.5 |
| Embodied Energy, MJ/kg | 77 | |
| 65 |
| Embodied Water, L/kg | 130 | |
| 210 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 33 to 150 | |
| 48 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 1690 | |
| 180 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 17 to 28 | |
| 18 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 18 |
| Thermal Shock Resistance, points | 16 to 26 | |
| 11 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0.2 to 0.6 |
| Chromium (Cr), % | 0 to 0.3 | |
| 28 to 32 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 50.7 to 56.5 | |
| 40.8 to 53.8 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 0 to 0.5 |
| Nickel (Ni), % | 43.5 to 46.5 | |
| 18 to 22 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 2.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.040 |