C14510 Copper vs. C95500 Bronze

Both C14510 copper and C95500 bronze are copper alloys. They have 81% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C14510 copper and the bottom bar is C95500 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 9.1 to 9.6
8.4 to 10
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 43
44
Tensile Strength: Ultimate (UTS), MPa 300 to 320
700 to 850
Tensile Strength: Yield (Proof), MPa 230 to 250
320 to 470

Thermal Properties

Latent Heat of Fusion, J/g 210
230
Maximum Temperature: Mechanical, °C 200
230
Melting Completion (Liquidus), °C 1080
1050
Melting Onset (Solidus), °C 1050
1040
Specific Heat Capacity, J/kg-K 390
450
Thermal Conductivity, W/m-K 360
42
Thermal Expansion, µm/m-K 17
18

Otherwise Unclassified Properties

Base Metal Price, % relative 33
28
Density, g/cm3 8.9
8.2
Embodied Carbon, kg CO2/kg material 2.6
3.5
Embodied Energy, MJ/kg 42
57
Embodied Water, L/kg 310
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 25 to 29
58 to 61
Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 280
420 to 950
Stiffness to Weight: Axial, points 7.2
8.0
Stiffness to Weight: Bending, points 18
20
Strength to Weight: Axial, points 9.2 to 10
24 to 29
Strength to Weight: Bending, points 11 to 12
21 to 24
Thermal Diffusivity, mm2/s 100
11
Thermal Shock Resistance, points 11 to 12
24 to 29

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
10 to 11.5
Copper (Cu), % 99.15 to 99.69
78 to 84
Iron (Fe), % 0
3.0 to 5.0
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0
0 to 3.5
Nickel (Ni), % 0
3.0 to 5.5
Phosphorus (P), % 0.010 to 0.030
0
Tellurium (Te), % 0.3 to 0.7
0
Residuals, % 0
0 to 0.5