C17000 Copper vs. AISI 403 Stainless Steel
C17000 copper belongs to the copper alloys classification, while AISI 403 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C17000 copper and the bottom bar is AISI 403 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 1.1 to 31 | |
| 16 to 25 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 45 | |
| 76 |
| Shear Strength, MPa | 320 to 750 | |
| 340 to 480 |
| Tensile Strength: Ultimate (UTS), MPa | 490 to 1310 | |
| 530 to 780 |
| Tensile Strength: Yield (Proof), MPa | 160 to 1140 | |
| 280 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 270 | |
| 740 |
| Melting Completion (Liquidus), °C | 980 | |
| 1450 |
| Melting Onset (Solidus), °C | 870 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 110 | |
| 28 |
| Thermal Expansion, µm/m-K | 17 | |
| 9.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 22 | |
| 3.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 1.9 |
| Embodied Energy, MJ/kg | 140 | |
| 27 |
| Embodied Water, L/kg | 310 | |
| 99 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.2 to 390 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 5420 | |
| 210 to 840 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 15 to 41 | |
| 19 to 28 |
| Strength to Weight: Bending, points | 16 to 30 | |
| 19 to 24 |
| Thermal Diffusivity, mm2/s | 32 | |
| 7.6 |
| Thermal Shock Resistance, points | 17 to 45 | |
| 20 to 29 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Beryllium (Be), % | 1.6 to 1.8 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 11.5 to 13 |
| Copper (Cu), % | 96.3 to 98.2 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 84.7 to 88.5 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 0 to 0.6 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Residuals, % | 0 to 0.5 | |
| 0 |