C17300 Copper vs. Ductile Cast Iron
C17300 copper belongs to the copper alloys classification, while ductile cast iron belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C17300 copper and the bottom bar is ductile cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 170 to 180 |
| Elongation at Break, % | 3.0 to 23 | |
| 2.1 to 20 |
| Poisson's Ratio | 0.33 | |
| 0.28 to 0.31 |
| Shear Modulus, GPa | 45 | |
| 64 to 70 |
| Shear Strength, MPa | 320 to 790 | |
| 420 to 800 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 1380 | |
| 460 to 920 |
| Tensile Strength: Yield (Proof), MPa | 160 to 1200 | |
| 310 to 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 270 | |
| 290 |
| Melting Completion (Liquidus), °C | 980 | |
| 1160 |
| Melting Onset (Solidus), °C | 870 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 490 |
| Thermal Conductivity, W/m-K | 110 | |
| 31 to 36 |
| Thermal Expansion, µm/m-K | 17 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 23 | |
| 8.8 to 9.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 7.1 to 7.5 |
| Embodied Carbon, kg CO2/kg material | 9.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 150 | |
| 21 |
| Embodied Water, L/kg | 310 | |
| 43 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 to 88 | |
| 17 to 80 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 5410 | |
| 280 to 1330 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 12 to 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 to 26 |
| Strength to Weight: Axial, points | 16 to 44 | |
| 17 to 35 |
| Strength to Weight: Bending, points | 16 to 31 | |
| 18 to 29 |
| Thermal Diffusivity, mm2/s | 32 | |
| 8.9 to 10 |
| Thermal Shock Resistance, points | 17 to 48 | |
| 17 to 35 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Beryllium (Be), % | 1.8 to 2.0 | |
| 0 |
| Carbon (C), % | 0 | |
| 3.0 to 3.5 |
| Copper (Cu), % | 95.5 to 97.8 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 93.7 to 95.5 |
| Lead (Pb), % | 0.2 to 0.6 | |
| 0 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.080 |
| Silicon (Si), % | 0 to 0.2 | |
| 1.5 to 2.8 |
| Residuals, % | 0 to 0.5 | |
| 0 |