C19700 Copper vs. C95500 Bronze
Both C19700 copper and C95500 bronze are copper alloys. They have 82% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C19700 copper and the bottom bar is C95500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 2.4 to 13 | |
| 8.4 to 10 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 530 | |
| 700 to 850 |
| Tensile Strength: Yield (Proof), MPa | 330 to 520 | |
| 320 to 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 230 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1050 |
| Melting Onset (Solidus), °C | 1040 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 450 |
| Thermal Conductivity, W/m-K | 250 | |
| 42 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 86 to 88 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 87 to 89 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 28 |
| Density, g/cm3 | 8.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.5 |
| Embodied Energy, MJ/kg | 41 | |
| 57 |
| Embodied Water, L/kg | 310 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 49 | |
| 58 to 61 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 460 to 1160 | |
| 420 to 950 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 8.0 |
| Stiffness to Weight: Bending, points | 18 | |
| 20 |
| Strength to Weight: Axial, points | 12 to 16 | |
| 24 to 29 |
| Strength to Weight: Bending, points | 14 to 16 | |
| 21 to 24 |
| Thermal Diffusivity, mm2/s | 73 | |
| 11 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 24 to 29 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 10 to 11.5 |
| Cobalt (Co), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 97.4 to 99.59 | |
| 78 to 84 |
| Iron (Fe), % | 0.3 to 1.2 | |
| 3.0 to 5.0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Magnesium (Mg), % | 0.010 to 0.2 | |
| 0 |
| Manganese (Mn), % | 0 to 0.050 | |
| 0 to 3.5 |
| Nickel (Ni), % | 0 to 0.050 | |
| 3.0 to 5.5 |
| Phosphorus (P), % | 0.1 to 0.4 | |
| 0 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.5 |