C31400 Bronze vs. C51000 Bronze
Both C31400 bronze and C51000 bronze are copper alloys. They have 89% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C31400 bronze and the bottom bar is C51000 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 6.8 to 29 | |
| 2.7 to 64 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 42 | |
| 42 |
| Shear Strength, MPa | 180 to 240 | |
| 250 to 460 |
| Tensile Strength: Ultimate (UTS), MPa | 270 to 420 | |
| 330 to 780 |
| Tensile Strength: Yield (Proof), MPa | 78 to 310 | |
| 130 to 750 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 190 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1050 |
| Melting Onset (Solidus), °C | 1010 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Conductivity, W/m-K | 180 | |
| 77 |
| Thermal Expansion, µm/m-K | 18 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 42 | |
| 18 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 43 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 33 |
| Density, g/cm3 | 8.8 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.1 |
| Embodied Energy, MJ/kg | 42 | |
| 50 |
| Embodied Water, L/kg | 310 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 to 59 | |
| 7.0 to 490 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 28 to 420 | |
| 75 to 2490 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 8.7 to 13 | |
| 10 to 25 |
| Strength to Weight: Bending, points | 11 to 14 | |
| 12 to 21 |
| Thermal Diffusivity, mm2/s | 54 | |
| 23 |
| Thermal Shock Resistance, points | 9.6 to 15 | |
| 12 to 28 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 87.5 to 90.5 | |
| 92.9 to 95.5 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.1 |
| Lead (Pb), % | 1.3 to 2.5 | |
| 0 to 0.050 |
| Nickel (Ni), % | 0 to 0.7 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.030 to 0.35 |
| Tin (Sn), % | 0 | |
| 4.5 to 5.8 |
| Zinc (Zn), % | 5.8 to 11.2 | |
| 0 to 0.3 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |