C43500 Brass vs. C32000 Brass
Both C43500 brass and C32000 brass are copper alloys. They have a moderately high 94% of their average alloy composition in common.
For each property being compared, the top bar is C43500 brass and the bottom bar is C32000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 8.5 to 46 | |
| 6.8 to 29 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 42 | |
| 41 |
| Shear Strength, MPa | 220 to 310 | |
| 180 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 530 | |
| 270 to 470 |
| Tensile Strength: Yield (Proof), MPa | 120 to 480 | |
| 78 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 170 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1020 |
| Melting Onset (Solidus), °C | 970 | |
| 990 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Conductivity, W/m-K | 120 | |
| 160 |
| Thermal Expansion, µm/m-K | 19 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 36 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 30 | |
| 37 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 28 |
| Density, g/cm3 | 8.5 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 45 | |
| 42 |
| Embodied Water, L/kg | 320 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 44 to 120 | |
| 30 to 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 65 to 1040 | |
| 28 to 680 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 10 to 17 | |
| 8.8 to 15 |
| Strength to Weight: Bending, points | 12 to 17 | |
| 11 to 16 |
| Thermal Diffusivity, mm2/s | 37 | |
| 47 |
| Thermal Shock Resistance, points | 11 to 18 | |
| 9.5 to 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 79 to 83 | |
| 83.5 to 86.5 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.090 | |
| 1.5 to 2.2 |
| Nickel (Ni), % | 0 | |
| 0 to 0.25 |
| Tin (Sn), % | 0.6 to 1.2 | |
| 0 |
| Zinc (Zn), % | 15.4 to 20.4 | |
| 10.6 to 15 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.4 |