C50100 Bronze vs. 3104 Aluminum

C50100 bronze belongs to the copper alloys classification, while 3104 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C50100 bronze and the bottom bar is 3104 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
70
Elongation at Break, % 40
1.1 to 20
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 43
26
Shear Strength, MPa 180
110 to 180
Tensile Strength: Ultimate (UTS), MPa 270
170 to 310
Tensile Strength: Yield (Proof), MPa 82
68 to 270

Thermal Properties

Latent Heat of Fusion, J/g 210
400
Maximum Temperature: Mechanical, °C 200
180
Melting Completion (Liquidus), °C 1080
650
Melting Onset (Solidus), °C 1070
600
Specific Heat Capacity, J/kg-K 380
900
Thermal Conductivity, W/m-K 230
160
Thermal Expansion, µm/m-K 17
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 55
41
Electrical Conductivity: Equal Weight (Specific), % IACS 55
130

Otherwise Unclassified Properties

Base Metal Price, % relative 31
9.5
Density, g/cm3 8.9
2.8
Embodied Carbon, kg CO2/kg material 2.6
8.4
Embodied Energy, MJ/kg 42
150
Embodied Water, L/kg 310
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
1.6 to 60
Resilience: Unit (Modulus of Resilience), kJ/m3 29
34 to 540
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
50
Strength to Weight: Axial, points 8.3
17 to 31
Strength to Weight: Bending, points 10
25 to 37
Thermal Diffusivity, mm2/s 66
64
Thermal Shock Resistance, points 9.5
7.6 to 13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
95.1 to 98.4
Copper (Cu), % 98.6 to 99.49
0.050 to 0.25
Gallium (Ga), % 0
0 to 0.050
Iron (Fe), % 0 to 0.050
0 to 0.8
Lead (Pb), % 0 to 0.050
0
Magnesium (Mg), % 0
0.8 to 1.3
Manganese (Mn), % 0
0.8 to 1.4
Phosphorus (P), % 0.010 to 0.050
0
Silicon (Si), % 0
0 to 0.6
Tin (Sn), % 0.5 to 0.8
0
Titanium (Ti), % 0
0 to 0.1
Vanadium (V), % 0
0 to 0.050
Zinc (Zn), % 0
0 to 0.25
Residuals, % 0 to 0.5
0 to 0.15