C50100 Bronze vs. AISI 310H Stainless Steel

C50100 bronze belongs to the copper alloys classification, while AISI 310H stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is AISI 310H stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 40
40
Poisson's Ratio 0.34
0.27
Shear Modulus, GPa 43
79
Shear Strength, MPa 180
400
Tensile Strength: Ultimate (UTS), MPa 270
580
Tensile Strength: Yield (Proof), MPa 82
230

Thermal Properties

Latent Heat of Fusion, J/g 210
300
Maximum Temperature: Mechanical, °C 200
1100
Melting Completion (Liquidus), °C 1080
1410
Melting Onset (Solidus), °C 1070
1360
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 230
15
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 55
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 55
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 31
25
Density, g/cm3 8.9
7.9
Embodied Carbon, kg CO2/kg material 2.6
4.3
Embodied Energy, MJ/kg 42
61
Embodied Water, L/kg 310
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
190
Resilience: Unit (Modulus of Resilience), kJ/m3 29
130
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 8.3
21
Strength to Weight: Bending, points 10
20
Thermal Diffusivity, mm2/s 66
3.9
Thermal Shock Resistance, points 9.5
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.040 to 0.1
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 98.6 to 99.49
0
Iron (Fe), % 0 to 0.050
49.1 to 57
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0
19 to 22
Phosphorus (P), % 0.010 to 0.050
0 to 0.045
Silicon (Si), % 0
0 to 0.75
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0.5 to 0.8
0
Residuals, % 0 to 0.5
0