C50100 Bronze vs. ASTM Grade HE Steel

C50100 bronze belongs to the copper alloys classification, while ASTM grade HE steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C50100 bronze and the bottom bar is ASTM grade HE steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 40
10
Poisson's Ratio 0.34
0.27
Shear Modulus, GPa 43
79
Tensile Strength: Ultimate (UTS), MPa 270
670
Tensile Strength: Yield (Proof), MPa 82
310

Thermal Properties

Latent Heat of Fusion, J/g 210
310
Maximum Temperature: Mechanical, °C 200
1100
Melting Completion (Liquidus), °C 1080
1400
Melting Onset (Solidus), °C 1070
1360
Specific Heat Capacity, J/kg-K 380
490
Thermal Conductivity, W/m-K 230
14
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 55
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 55
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
19
Density, g/cm3 8.9
7.7
Embodied Carbon, kg CO2/kg material 2.6
3.5
Embodied Energy, MJ/kg 42
50
Embodied Water, L/kg 310
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
56
Resilience: Unit (Modulus of Resilience), kJ/m3 29
240
Stiffness to Weight: Axial, points 7.2
15
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 8.3
24
Strength to Weight: Bending, points 10
22
Thermal Diffusivity, mm2/s 66
3.6
Thermal Shock Resistance, points 9.5
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.2 to 0.5
Chromium (Cr), % 0
26 to 30
Copper (Cu), % 98.6 to 99.49
0
Iron (Fe), % 0 to 0.050
53.9 to 65.8
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
8.0 to 11
Phosphorus (P), % 0.010 to 0.050
0 to 0.040
Silicon (Si), % 0
0 to 2.0
Sulfur (S), % 0
0 to 0.040
Tin (Sn), % 0.5 to 0.8
0
Residuals, % 0 to 0.5
0