C50100 Bronze vs. AWS E33-31
C50100 bronze belongs to the copper alloys classification, while AWS E33-31 belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is C50100 bronze and the bottom bar is AWS E33-31.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 210 |
| Elongation at Break, % | 40 | |
| 29 |
| Poisson's Ratio | 0.34 | |
| 0.27 |
| Shear Modulus, GPa | 43 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 320 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1380 |
| Melting Onset (Solidus), °C | 1070 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 480 |
| Thermal Expansion, µm/m-K | 17 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 36 |
| Density, g/cm3 | 8.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 6.0 |
| Embodied Energy, MJ/kg | 42 | |
| 86 |
| Embodied Water, L/kg | 310 | |
| 260 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 8.3 | |
| 28 |
| Strength to Weight: Bending, points | 10 | |
| 24 |
| Thermal Shock Resistance, points | 9.5 | |
| 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 31 to 35 |
| Copper (Cu), % | 98.6 to 99.49 | |
| 0.4 to 0.8 |
| Iron (Fe), % | 0 to 0.050 | |
| 24.7 to 34.8 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 2.5 to 4.0 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 30 to 32 |
| Nitrogen (N), % | 0 | |
| 0.3 to 0.5 |
| Phosphorus (P), % | 0.010 to 0.050 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.9 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 0.5 to 0.8 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |