C63020 Bronze vs. C92900 Bronze

Both C63020 bronze and C92900 bronze are copper alloys. They have 82% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C63020 bronze and the bottom bar is C92900 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Elongation at Break, % 6.8
9.1
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 44
40
Tensile Strength: Ultimate (UTS), MPa 1020
350
Tensile Strength: Yield (Proof), MPa 740
190

Thermal Properties

Latent Heat of Fusion, J/g 230
190
Maximum Temperature: Mechanical, °C 230
170
Melting Completion (Liquidus), °C 1070
1030
Melting Onset (Solidus), °C 1020
860
Specific Heat Capacity, J/kg-K 450
370
Thermal Conductivity, W/m-K 40
58
Thermal Expansion, µm/m-K 18
18

Otherwise Unclassified Properties

Base Metal Price, % relative 29
35
Density, g/cm3 8.2
8.8
Embodied Carbon, kg CO2/kg material 3.6
3.8
Embodied Energy, MJ/kg 58
61
Embodied Water, L/kg 390
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
27
Resilience: Unit (Modulus of Resilience), kJ/m3 2320
170
Stiffness to Weight: Axial, points 8.0
6.8
Stiffness to Weight: Bending, points 20
18
Strength to Weight: Axial, points 34
11
Strength to Weight: Bending, points 27
13
Thermal Diffusivity, mm2/s 11
18
Thermal Shock Resistance, points 35
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 10 to 11
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Chromium (Cr), % 0 to 0.050
0
Cobalt (Co), % 0 to 0.2
0
Copper (Cu), % 74.7 to 81.8
82 to 86
Iron (Fe), % 4.0 to 5.5
0 to 0.2
Lead (Pb), % 0 to 0.030
2.0 to 3.2
Manganese (Mn), % 0 to 1.5
0
Nickel (Ni), % 4.2 to 6.0
2.8 to 4.0
Phosphorus (P), % 0
0 to 1.5
Silicon (Si), % 0
0 to 0.0050
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0 to 0.25
9.0 to 11
Zinc (Zn), % 0 to 0.3
0 to 0.25
Residuals, % 0 to 0.5
0 to 0.7