C65500 Bronze vs. AISI 422 Stainless Steel
C65500 bronze belongs to the copper alloys classification, while AISI 422 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C65500 bronze and the bottom bar is AISI 422 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 4.0 to 70 | |
| 15 to 17 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 43 | |
| 76 |
| Shear Strength, MPa | 260 to 440 | |
| 560 to 660 |
| Tensile Strength: Ultimate (UTS), MPa | 360 to 760 | |
| 910 to 1080 |
| Tensile Strength: Yield (Proof), MPa | 120 to 430 | |
| 670 to 870 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 650 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1480 |
| Melting Onset (Solidus), °C | 970 | |
| 1470 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 470 |
| Thermal Conductivity, W/m-K | 36 | |
| 24 |
| Thermal Expansion, µm/m-K | 18 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 4.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.3 | |
| 5.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 11 |
| Density, g/cm3 | 8.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.1 |
| Embodied Energy, MJ/kg | 42 | |
| 44 |
| Embodied Water, L/kg | 300 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 450 | |
| 140 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 62 to 790 | |
| 1140 to 1910 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 12 to 24 | |
| 32 to 38 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 26 to 30 |
| Thermal Diffusivity, mm2/s | 10 | |
| 6.4 |
| Thermal Shock Resistance, points | 12 to 26 | |
| 33 to 39 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0.2 to 0.25 |
| Chromium (Cr), % | 0 | |
| 11 to 12.5 |
| Copper (Cu), % | 91.5 to 96.7 | |
| 0 |
| Iron (Fe), % | 0 to 0.8 | |
| 81.9 to 85.8 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0.5 to 1.3 | |
| 0.5 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0.9 to 1.3 |
| Nickel (Ni), % | 0 to 0.6 | |
| 0.5 to 1.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 2.8 to 3.8 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Tungsten (W), % | 0 | |
| 0.9 to 1.3 |
| Vanadium (V), % | 0 | |
| 0.2 to 0.3 |
| Zinc (Zn), % | 0 to 1.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |