C67600 Bronze vs. AWS BAg-2a
C67600 bronze belongs to the copper alloys classification, while AWS BAg-2a belongs to the otherwise unclassified metals. They have 50% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is C67600 bronze and the bottom bar is AWS BAg-2a.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 83 |
| Poisson's Ratio | 0.31 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 570 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 130 |
| Melting Completion (Liquidus), °C | 890 | |
| 710 |
| Melting Onset (Solidus), °C | 870 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 310 |
| Thermal Expansion, µm/m-K | 21 | |
| 23 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.0 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 30 |
| Embodied Energy, MJ/kg | 47 | |
| 470 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 5.2 |
| Stiffness to Weight: Bending, points | 20 | |
| 17 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 5.4 |
| Strength to Weight: Bending, points | 16 to 19 | |
| 7.8 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 6.5 |
Alloy Composition
| Cadmium (Cd), % | 0 | |
| 19 to 21 |
| Copper (Cu), % | 57 to 60 | |
| 26 to 28 |
| Iron (Fe), % | 0.4 to 1.3 | |
| 0 |
| Lead (Pb), % | 0.5 to 1.0 | |
| 0 |
| Manganese (Mn), % | 0.050 to 0.5 | |
| 0 |
| Silver (Ag), % | 0 | |
| 29 to 31 |
| Tin (Sn), % | 0.5 to 1.5 | |
| 0 |
| Zinc (Zn), % | 35.2 to 41.6 | |
| 21 to 25 |
| Residuals, % | 0 | |
| 0 to 0.15 |