C69400 Brass vs. C31600 Bronze
Both C69400 brass and C31600 bronze are copper alloys. They have 90% of their average alloy composition in common.
For each property being compared, the top bar is C69400 brass and the bottom bar is C31600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 17 | |
| 6.7 to 28 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 42 | |
| 42 |
| Shear Strength, MPa | 350 | |
| 170 to 270 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 270 to 460 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 80 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 180 |
| Melting Completion (Liquidus), °C | 920 | |
| 1040 |
| Melting Onset (Solidus), °C | 820 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 380 |
| Thermal Conductivity, W/m-K | 26 | |
| 140 |
| Thermal Expansion, µm/m-K | 18 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.2 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.7 | |
| 33 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 29 |
| Density, g/cm3 | 8.3 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 44 | |
| 43 |
| Embodied Water, L/kg | 300 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 80 | |
| 30 to 58 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 340 | |
| 28 to 690 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 19 | |
| 8.5 to 15 |
| Strength to Weight: Bending, points | 18 | |
| 11 to 15 |
| Thermal Diffusivity, mm2/s | 7.7 | |
| 42 |
| Thermal Shock Resistance, points | 20 | |
| 9.4 to 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 80 to 83 | |
| 87.5 to 90.5 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.3 | |
| 1.3 to 2.5 |
| Nickel (Ni), % | 0 | |
| 0.7 to 1.2 |
| Phosphorus (P), % | 0 | |
| 0.040 to 0.1 |
| Silicon (Si), % | 3.5 to 4.5 | |
| 0 |
| Zinc (Zn), % | 11.5 to 16.5 | |
| 5.2 to 10.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.4 |