C73500 Nickel Silver vs. C97400 Nickel Silver

Both C73500 nickel silver and C97400 nickel silver are copper alloys. They have 86% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C73500 nickel silver and the bottom bar is C97400 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 130
120
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 47
44
Tensile Strength: Ultimate (UTS), MPa 380 to 580
260

Thermal Properties

Latent Heat of Fusion, J/g 210
190
Maximum Temperature: Mechanical, °C 220
180
Melting Completion (Liquidus), °C 1140
1100
Melting Onset (Solidus), °C 1090
1070
Specific Heat Capacity, J/kg-K 400
380
Thermal Conductivity, W/m-K 36
27
Thermal Expansion, µm/m-K 17
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.5
6.0
Electrical Conductivity: Equal Weight (Specific), % IACS 6.7
6.3

Otherwise Unclassified Properties

Base Metal Price, % relative 35
33
Density, g/cm3 8.7
8.6
Embodied Carbon, kg CO2/kg material 4.0
4.1
Embodied Energy, MJ/kg 61
64
Embodied Water, L/kg 300
320

Common Calculations

Stiffness to Weight: Axial, points 8.0
7.5
Stiffness to Weight: Bending, points 19
19
Strength to Weight: Axial, points 12 to 19
8.5
Strength to Weight: Bending, points 13 to 18
11
Thermal Diffusivity, mm2/s 10
8.3
Thermal Shock Resistance, points 13 to 19
8.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 70.5 to 73.5
58 to 61
Iron (Fe), % 0 to 0.25
0 to 1.5
Lead (Pb), % 0 to 0.1
4.5 to 5.5
Manganese (Mn), % 0 to 0.5
0 to 0.5
Nickel (Ni), % 16.5 to 19.5
15.5 to 17
Tin (Sn), % 0
2.5 to 3.5
Zinc (Zn), % 5.7 to 13
10 to 19.5
Residuals, % 0 to 0.5
0 to 1.0