C79600 Nickel Silver vs. EN 1.0491 Steel

C79600 nickel silver belongs to the copper alloys classification, while EN 1.0491 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is EN 1.0491 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 15
26
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 43
73
Shear Strength, MPa 290
280
Tensile Strength: Ultimate (UTS), MPa 480
440
Tensile Strength: Yield (Proof), MPa 300
270

Thermal Properties

Latent Heat of Fusion, J/g 180
250
Maximum Temperature: Mechanical, °C 130
400
Melting Completion (Liquidus), °C 930
1460
Melting Onset (Solidus), °C 880
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 36
47
Thermal Expansion, µm/m-K 21
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.4
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.5
1.6
Embodied Energy, MJ/kg 57
21
Embodied Water, L/kg 310
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
99
Resilience: Unit (Modulus of Resilience), kJ/m3 400
200
Stiffness to Weight: Axial, points 7.8
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 17
16
Strength to Weight: Bending, points 17
16
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 15
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.015
Carbon (C), % 0
0 to 0.18
Chromium (Cr), % 0
0 to 0.35
Copper (Cu), % 43.5 to 46.5
0 to 0.6
Iron (Fe), % 0
96.1 to 99.55
Lead (Pb), % 0.8 to 1.2
0
Manganese (Mn), % 1.5 to 2.5
0.45 to 1.6
Molybdenum (Mo), % 0
0 to 0.13
Nickel (Ni), % 9.0 to 11
0 to 0.35
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.017
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.45
Sulfur (S), % 0
0 to 0.025
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0
0 to 0.070
Zinc (Zn), % 38.3 to 45.2
0
Residuals, % 0 to 0.5
0