C79600 Nickel Silver vs. S44700 Stainless Steel

C79600 nickel silver belongs to the copper alloys classification, while S44700 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is S44700 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
210
Elongation at Break, % 15
23
Poisson's Ratio 0.3
0.27
Shear Modulus, GPa 43
82
Shear Strength, MPa 290
380
Tensile Strength: Ultimate (UTS), MPa 480
600
Tensile Strength: Yield (Proof), MPa 300
450

Thermal Properties

Latent Heat of Fusion, J/g 180
300
Maximum Temperature: Mechanical, °C 130
1100
Melting Completion (Liquidus), °C 930
1460
Melting Onset (Solidus), °C 880
1410
Specific Heat Capacity, J/kg-K 390
480
Thermal Expansion, µm/m-K 21
11

Otherwise Unclassified Properties

Base Metal Price, % relative 25
18
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.5
3.6
Embodied Energy, MJ/kg 57
49
Embodied Water, L/kg 310
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
120
Resilience: Unit (Modulus of Resilience), kJ/m3 400
480
Stiffness to Weight: Axial, points 7.8
15
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 17
20
Thermal Shock Resistance, points 15
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.010
Chromium (Cr), % 0
28 to 30
Copper (Cu), % 43.5 to 46.5
0 to 0.15
Iron (Fe), % 0
64.9 to 68.5
Lead (Pb), % 0.8 to 1.2
0
Manganese (Mn), % 1.5 to 2.5
0 to 0.3
Molybdenum (Mo), % 0
3.5 to 4.2
Nickel (Ni), % 9.0 to 11
0 to 0.15
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.2
Sulfur (S), % 0
0 to 0.020
Zinc (Zn), % 38.3 to 45.2
0
Residuals, % 0 to 0.5
0