C82800 Copper vs. C99400 Brass
Both C82800 copper and C99400 brass are copper alloys. They have a moderately high 91% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C82800 copper and the bottom bar is C99400 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 46 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 1140 | |
| 460 to 550 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1000 | |
| 230 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 200 |
| Melting Completion (Liquidus), °C | 930 | |
| 1070 |
| Melting Onset (Solidus), °C | 890 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 17 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 19 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 2.8 |
| Embodied Energy, MJ/kg | 190 | |
| 45 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 590 to 4080 | |
| 230 to 590 |
| Stiffness to Weight: Axial, points | 7.8 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 21 to 36 | |
| 15 to 17 |
| Strength to Weight: Bending, points | 20 to 28 | |
| 15 to 17 |
| Thermal Shock Resistance, points | 23 to 39 | |
| 16 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.15 | |
| 0.5 to 2.0 |
| Beryllium (Be), % | 2.5 to 2.9 | |
| 0 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Cobalt (Co), % | 0.15 to 0.7 | |
| 0 |
| Copper (Cu), % | 94.6 to 97.2 | |
| 83.5 to 96.5 |
| Iron (Fe), % | 0 to 0.25 | |
| 1.0 to 3.0 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 to 0.25 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 0.2 | |
| 1.0 to 3.5 |
| Silicon (Si), % | 0.2 to 0.35 | |
| 0.5 to 2.0 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 |
| Titanium (Ti), % | 0 to 0.12 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0.5 to 5.0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.3 |