C84000 Brass vs. EN 1.8918 Steel

C84000 brass belongs to the copper alloys classification, while EN 1.8918 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is EN 1.8918 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
190
Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 27
19
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 42
73
Tensile Strength: Ultimate (UTS), MPa 250
640
Tensile Strength: Yield (Proof), MPa 140
490

Thermal Properties

Latent Heat of Fusion, J/g 190
250
Maximum Temperature: Mechanical, °C 170
400
Melting Completion (Liquidus), °C 1040
1460
Melting Onset (Solidus), °C 940
1420
Specific Heat Capacity, J/kg-K 380
470
Thermal Conductivity, W/m-K 72
46
Thermal Expansion, µm/m-K 18
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 16
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 17
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 30
2.5
Density, g/cm3 8.6
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.7
Embodied Energy, MJ/kg 49
24
Embodied Water, L/kg 330
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 58
110
Resilience: Unit (Modulus of Resilience), kJ/m3 83
640
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 8.2
23
Strength to Weight: Bending, points 10
21
Thermal Diffusivity, mm2/s 22
12
Thermal Shock Resistance, points 9.0
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0.020 to 0.050
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0 to 0.2
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 82 to 89
0 to 0.7
Iron (Fe), % 0 to 0.4
95.2 to 98.9
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
1.1 to 1.7
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0.5 to 2.0
0 to 0.8
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.025
Phosphorus (P), % 0 to 0.050
0 to 0.020
Silicon (Si), % 0 to 0.0050
0 to 0.6
Sulfur (S), % 0.1 to 0.65
0 to 0.0050
Tin (Sn), % 2.0 to 4.0
0
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.2
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0