C85900 Brass vs. EN 1.1191 Steel
C85900 brass belongs to the copper alloys classification, while EN 1.1191 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C85900 brass and the bottom bar is EN 1.1191 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 85 | |
| 180 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 30 | |
| 16 to 17 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 460 | |
| 630 to 700 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 310 to 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 400 |
| Melting Completion (Liquidus), °C | 830 | |
| 1460 |
| Melting Onset (Solidus), °C | 790 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 89 | |
| 48 |
| Thermal Expansion, µm/m-K | 20 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 28 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 2.1 |
| Density, g/cm3 | 8.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 49 | |
| 19 |
| Embodied Water, L/kg | 330 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 83 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 260 to 510 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 16 | |
| 22 to 25 |
| Strength to Weight: Bending, points | 17 | |
| 21 to 22 |
| Thermal Diffusivity, mm2/s | 29 | |
| 13 |
| Thermal Shock Resistance, points | 16 | |
| 20 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0.1 to 0.6 | |
| 0 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 |
| Boron (B), % | 0 to 0.2 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.42 to 0.5 |
| Chromium (Cr), % | 0 | |
| 0 to 0.4 |
| Copper (Cu), % | 58 to 62 | |
| 0 |
| Iron (Fe), % | 0 to 0.5 | |
| 97.3 to 99.08 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 |
| Manganese (Mn), % | 0 to 0.010 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 1.5 | |
| 0 to 0.4 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.25 | |
| 0 to 0.4 |
| Sulfur (S), % | 0.1 to 0.65 | |
| 0 to 0.035 |
| Tin (Sn), % | 0 to 1.5 | |
| 0 |
| Zinc (Zn), % | 31 to 41 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.7 | |
| 0 |