C85900 Brass vs. SAE-AISI 1090 Steel
C85900 brass belongs to the copper alloys classification, while SAE-AISI 1090 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C85900 brass and the bottom bar is SAE-AISI 1090 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 85 | |
| 220 to 280 |
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 30 | |
| 11 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 460 | |
| 790 to 950 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 520 to 610 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 400 |
| Melting Completion (Liquidus), °C | 830 | |
| 1450 |
| Melting Onset (Solidus), °C | 790 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 89 | |
| 50 |
| Thermal Expansion, µm/m-K | 20 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 28 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 1.8 |
| Density, g/cm3 | 8.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 49 | |
| 19 |
| Embodied Water, L/kg | 330 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 82 to 91 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 730 to 1000 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 16 | |
| 28 to 34 |
| Strength to Weight: Bending, points | 17 | |
| 24 to 27 |
| Thermal Diffusivity, mm2/s | 29 | |
| 13 |
| Thermal Shock Resistance, points | 16 | |
| 25 to 31 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0.1 to 0.6 | |
| 0 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 |
| Boron (B), % | 0 to 0.2 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.85 to 1.0 |
| Copper (Cu), % | 58 to 62 | |
| 0 |
| Iron (Fe), % | 0 to 0.5 | |
| 98 to 98.6 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 |
| Manganese (Mn), % | 0 to 0.010 | |
| 0.6 to 0.9 |
| Nickel (Ni), % | 0 to 1.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.25 | |
| 0 |
| Sulfur (S), % | 0.1 to 0.65 | |
| 0 to 0.050 |
| Tin (Sn), % | 0 to 1.5 | |
| 0 |
| Zinc (Zn), % | 31 to 41 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.7 | |
| 0 |