C86300 Bronze vs. C19200 Copper

Both C86300 bronze and C19200 copper are copper alloys. They have 64% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C86300 bronze and the bottom bar is C19200 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
120
Elongation at Break, % 14
2.0 to 35
Poisson's Ratio 0.32
0.34
Shear Modulus, GPa 42
44
Tensile Strength: Ultimate (UTS), MPa 850
280 to 530
Tensile Strength: Yield (Proof), MPa 480
98 to 510

Thermal Properties

Latent Heat of Fusion, J/g 200
210
Maximum Temperature: Mechanical, °C 160
200
Melting Completion (Liquidus), °C 920
1080
Melting Onset (Solidus), °C 890
1080
Specific Heat Capacity, J/kg-K 420
390
Thermal Conductivity, W/m-K 35
240
Thermal Expansion, µm/m-K 20
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
58 to 74
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
58 to 75

Otherwise Unclassified Properties

Base Metal Price, % relative 23
30
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 3.0
2.6
Embodied Energy, MJ/kg 51
41
Embodied Water, L/kg 360
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
10 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 1030
42 to 1120
Stiffness to Weight: Axial, points 7.8
7.2
Stiffness to Weight: Bending, points 20
18
Strength to Weight: Axial, points 30
8.8 to 17
Strength to Weight: Bending, points 25
11 to 16
Thermal Diffusivity, mm2/s 11
69
Thermal Shock Resistance, points 28
10 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.0 to 7.5
0
Copper (Cu), % 60 to 66
98.5 to 99.19
Iron (Fe), % 2.0 to 4.0
0.8 to 1.2
Lead (Pb), % 0 to 0.2
0 to 0.030
Manganese (Mn), % 2.5 to 5.0
0
Nickel (Ni), % 0 to 1.0
0
Phosphorus (P), % 0
0.010 to 0.040
Tin (Sn), % 0 to 0.2
0
Zinc (Zn), % 22 to 28
0 to 0.2
Residuals, % 0 to 1.0
0 to 0.2