C92900 Bronze vs. CC750S Brass
Both C92900 bronze and CC750S brass are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 68% of their average alloy composition in common.
For each property being compared, the top bar is C92900 bronze and the bottom bar is CC750S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 84 | |
| 54 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 9.1 | |
| 13 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 40 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 200 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 80 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 130 |
| Melting Completion (Liquidus), °C | 1030 | |
| 860 |
| Melting Onset (Solidus), °C | 860 | |
| 810 |
| Specific Heat Capacity, J/kg-K | 370 | |
| 380 |
| Thermal Conductivity, W/m-K | 58 | |
| 110 |
| Thermal Expansion, µm/m-K | 18 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 24 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.2 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 35 | |
| 25 |
| Density, g/cm3 | 8.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 3.8 | |
| 2.8 |
| Embodied Energy, MJ/kg | 61 | |
| 46 |
| Embodied Water, L/kg | 390 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 | |
| 22 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 30 |
| Stiffness to Weight: Axial, points | 6.8 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 11 | |
| 6.8 |
| Strength to Weight: Bending, points | 13 | |
| 9.3 |
| Thermal Diffusivity, mm2/s | 18 | |
| 35 |
| Thermal Shock Resistance, points | 13 | |
| 6.7 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.1 |
| Antimony (Sb), % | 0 to 0.25 | |
| 0 |
| Copper (Cu), % | 82 to 86 | |
| 62 to 67 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.8 |
| Lead (Pb), % | 2.0 to 3.2 | |
| 1.0 to 3.0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 2.8 to 4.0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 1.5 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Tin (Sn), % | 9.0 to 11 | |
| 0 to 1.5 |
| Zinc (Zn), % | 0 to 0.25 | |
| 26.3 to 36 |
| Residuals, % | 0 to 0.7 | |
| 0 |