K93050 Alloy vs. K93600 Alloy
Both K93050 alloy and K93600 alloy are iron alloys. There are 11 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is K93050 alloy and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 680 | |
| 480 to 810 |
Thermal Properties
| Melting Onset (Solidus), °C | 1380 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 520 |
| Thermal Expansion, µm/m-K | 12 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 23 | |
| 21 |
| Strength to Weight: Axial, points | 17 to 23 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 17 to 24 |
| Thermal Shock Resistance, points | 16 to 21 | |
| 34 to 57 |