K93600 Alloy vs. 85-silver 15-nickel
K93600 alloy belongs to the iron alloys classification, while 85-silver 15-nickel belongs to the otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is 85-silver 15-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
88 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
260 to 470 |
Thermal Properties
Melting Onset (Solidus), °C | 1430 | |
960 |
Specific Heat Capacity, J/kg-K | 520 | |
270 |
Thermal Expansion, µm/m-K | 7.3 | |
18 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
86 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
75 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
10 |
Common Calculations
Stiffness to Weight: Axial, points | 9.4 | |
4.8 |
Stiffness to Weight: Bending, points | 21 | |
14 |
Strength to Weight: Axial, points | 16 to 28 | |
7.1 to 13 |
Strength to Weight: Bending, points | 17 to 24 | |
8.9 to 13 |
Thermal Shock Resistance, points | 34 to 57 | |
12 to 21 |